Laser Cladding of MCrAlY coatings on stainless steel
MCrAlY alloys (where M stands for Ni,Co or both) are commonly used as overlay protective coatings in gas turbine engine components against high temperature oxidation and corrosion. The protective effect of these alloys is due to the formation of a continuous thermally stable oxide layer on the coati...
| Autores: | , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2014 |
| País: | España |
| Institución: | Universitat Politècnica de València (UPV) |
| Repositorio: | RiuNet. Repositorio Institucional de la Universitat Politécnica de Valéncia |
| Idioma: | inglés |
| OAI Identifier: | oai:riunet.upv.es:10251/59983 |
| Acceso en línea: | https://riunet.upv.es/handle/10251/59983 |
| Access Level: | acceso abierto |
| Palabra clave: | MCrAlY Laser cladding Coating CIENCIA DE LOS MATERIALES E INGENIERIA METALURGICA |
| Sumario: | MCrAlY alloys (where M stands for Ni,Co or both) are commonly used as overlay protective coatings in gas turbine engine components against high temperature oxidation and corrosion. The protective effect of these alloys is due to the formation of a continuous thermally stable oxide layer on the coating surface. In this work several types of MCrAlY alloys, differing in their elemental composition, have been deposited on austenitic stainless steel by means of laser cladding. The microstructure of the coatings have been characterized by SEM-EDS and XRD. As expected, elemental composition compatible with γ-Ni/γ'-Ni3Al, β-Ni/β'-NiAl or γCo/β-(Co,Ni)Al phases are observed in hypoeutectic or hypereutectic microstructures depending on the alloy composition. The high temperature oxidation behavior of the coatings was evaluated by air furnace oxidation tests at 1100ºC for 200 h. The oxidized surface of the samples was examined by SEM-EDS and the oxides present identified by theoretical stoichiometric calculations. Results indicate the formation of a uniform Al3O2 protective oxide scale with NiO, CoO, Y2O3/YAlO3 and Cr2O3 oxide inclusions. |
|---|