Supplementary Materials for Use of green Fs lasers to generate a superhydrophobic behavior in the surface of wind turbine blades
Supplementary Table S1: Examples of different topographies obtained with several laser treatments and the corresponding contact angle measurements. Figure S1. Photograph of the sample surface after performing the same laser treatment in air and in Ar. Experiments were carried out with Epulse = 48.5...
| Authors: | , , , |
|---|---|
| Format: | conjunto de datos |
| Publication Date: | 2022 |
| Country: | España |
| Institution: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repository: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/329632 |
| Online Access: | http://hdl.handle.net/10261/329632 |
| Access Level: | Open access |
| Summary: | Supplementary Table S1: Examples of different topographies obtained with several laser treatments and the corresponding contact angle measurements. Figure S1. Photograph of the sample surface after performing the same laser treatment in air and in Ar. Experiments were carried out with Epulse = 48.5 μJ/pulse, vlaser = 9 mm/s and and dlines = 65 μm. Sample dimensions are 4 cm × 4 cm and the laser treated regions are 1.5 cm × 1.5 cm. Figure S2. FESEM images of the processed sample surface with Epulse = 8.8 μJ/pulse. Other laser processing parameters included vlaser = 9 mm/s and dlines = 65 μm. |
|---|