Tantalum Alloy Welding: Does the Thermal Cycle Influence the Microstructure?
[EN] The aim of the present work is to verify the microstructural behavior of a B 521 tantalum alloy UNS Grade R05200 after welding, in relation to the welding thermal cycle. The joint design was a 1.5 mm thickness circumferential butt welding, on a 32 mm outside diameter pipe, welded in 1 G positio...
| Autores: | , , , , , , |
|---|---|
| Formato: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2022 |
| País: | España |
| Recursos: | Ajuntament de Barcelona |
| Repositorio: | BULERIA. Repositorio Institucional de la Universidad de León |
| OAI Identifier: | oai:buleria.unileon.es:10612/17545 |
| Acesso em linha: | https://hdl.handle.net/10612/17545 |
| Access Level: | acceso abierto |
| Palavra-chave: | Tecnología de materiales Tantalum welding Microstructure Heat-affected zone 3316.14 Soldaduras 3310.05 Ingeniería de Procesos |
| Resumo: | [EN] The aim of the present work is to verify the microstructural behavior of a B 521 tantalum alloy UNS Grade R05200 after welding, in relation to the welding thermal cycle. The joint design was a 1.5 mm thickness circumferential butt welding, on a 32 mm outside diameter pipe, welded in 1 G position (horizontal, flat, and rotating). The chosen welding process was gas tungsten arc welding (GTAW). The microstructural analysis showed the presence of coarse, dendritic-columnar structures, as well as a hexagonal cell, with no cracks noted. Hardness tests showed an increase in hardness, from 120 HV to 425 HV, in the heat-affected zone. Through finite element methods, the behavior of the temperature field was estimated and compared. |
|---|