Direct utilization of lignite coal in a Co–CeO2/YSZ/Ag solid oxide fuel cell
The feasibility of employing lignite coal as a fuel in a Direct Carbon Fuel Cell (DCFC) of the type: lignite|Co–CeO2/YSZ/Ag|air is investigated. The impact of several parameters, related to anodic electrode composition (20, 40 and 60 wt.% Co/CeO2), cell temperature (700–800 °C), carrier gas composit...
| Autores: | , , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión aceptada para publicación |
| Fecha de publicación: | 2015 |
| País: | España |
| Institución: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/132846 |
| Acceso en línea: | http://hdl.handle.net/10261/132846 |
| Access Level: | acceso abierto |
| Palabra clave: | Direct carbon fuel cells Lignite fuel Co/CeO2 anode Carbonates |
| Sumario: | The feasibility of employing lignite coal as a fuel in a Direct Carbon Fuel Cell (DCFC) of the type: lignite|Co–CeO2/YSZ/Ag|air is investigated. The impact of several parameters, related to anodic electrode composition (20, 40 and 60 wt.% Co/CeO2), cell temperature (700–800 °C), carrier gas composition (CO2/He mixtures), and total feed flow rate (10–70 cm3/min), was systematically examined. The effect of molten carbonates on DCFC performance was also investigated by employing a eutectic mixture of lithium and potassium carbonates as carbon additives. In the absence of carbonates, the optimum performance (∼10 mW cm−2 at 800 °C), was achieved by employing 20 wt.% Co/CeO2 as anodic electrode and pure CO2 as purging gas. An inferior behavior was demonstrated by utilizing He instead of CO2 atmosphere in anode compartment and by increasing purging gas flow rate. Carbonates infusion into lignite feedstock resulted in a further increase of maximum power density up to 32%. The obtained findings are discussed based also on AC impedance spectroscopy measurements, which revealed the impact of DCFC operating parameters on both ohmic and electrode resistances. |
|---|