Fatigue crack initiation and damage characterization in Brazilian test specimens for adhesive joints
The present study is focused on the fatigue failure initiation at bimaterial corners by means of a configuration based on the Brazilian disc specimens. These specimens were previously used for the generalized fracture toughness determination and prediction of failure in adhesive joints, carried out...
| Authors: | , , , , |
|---|---|
| Format: | article |
| Status: | Versión aceptada para publicación |
| Publication Date: | 2014 |
| Country: | España |
| Institution: | Universidad de Sevilla (US) |
| Repository: | idUS. Depósito de Investigación de la Universidad de Sevilla |
| OAI Identifier: | oai:idus.us.es:11441/158923 |
| Online Access: | https://hdl.handle.net/11441/158923 https://doi.org/10.1080/01694243.2012.698099 |
| Access Level: | Open access |
| Keyword: | Adhesive joints Failure Crack initiation Composites Fatigue |
| Summary: | The present study is focused on the fatigue failure initiation at bimaterial corners by means of a configuration based on the Brazilian disc specimens. These specimens were previously used for the generalized fracture toughness determination and prediction of failure in adhesive joints, carried out under static compressive loading. Under static loading, local yielding effects might affect the asymptotic two-dimensional linear elastic stress representation under consideration. Fatigue loading avoids this fact due to the lower load levels used. The present tests were performed using load control; video microscopy and still cameras were used for monitoring initiation and crack growth. The fatigue tests were halted periodically and images of the corner were taken where fatigue damage was anticipated. Damage initiation and subsequent crack growth were observed in some specimens, especially in those which presented brittle failure under static and fatigue tests. These analyses allowed the characterization of damage initiation for a typical bimaterial corner that can be found in composite to aluminium adhesive lap joints. |
|---|