Highly electroactive N–Fe hydrothermal carbons and carbon nanotubes for the oxygen reduction reaction
Glucose-derived carbons were prepared by hydrothermal carbonization of glucose followed by carbonization or activation to obtain carbon materials with different microporosities. These microporous carbons and carbon nanotubes (CNTs) were functionalized with melamine and/or iron(II) phthalocyanine (Fe...
| Autores: | , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión aceptada para publicación |
| Fecha de publicación: | 2020 |
| País: | España |
| Institución: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/414818 |
| Acceso en línea: | http://hdl.handle.net/10261/414818 https://api.elsevier.com/content/abstract/scopus_id/85083194659 |
| Access Level: | acceso abierto |
| Palabra clave: | Oxygen reduction reaction Carbon nanotubes Electrocatalysis Hydrothermal carbons Iron(II) phthalocyanine http://metadata.un.org/sdg/9 http://metadata.un.org/sdg/7 Ensure access to affordable, reliable, sustainable and modern energy for all Build resilient infrastructure, promote inclusive and sustainable industrialization and foster innovation |
| Sumario: | Glucose-derived carbons were prepared by hydrothermal carbonization of glucose followed by carbonization or activation to obtain carbon materials with different microporosities. These microporous carbons and carbon nanotubes (CNTs) were functionalized with melamine and/or iron(II) phthalocyanine (FePc) following three different methodologies: (i) functionalization with melamine via thermal treatment, (ii) incorporation of the lowest amount of FePc reported in the literature via incipient wetness impregnation followed by thermal treatment and (iii) functionalization with melamine followed by FePc incorporation. The chemical and textural characterization of the prepared materials and their electrochemical assessment allowed to understand the role of microporosity in the incorporation of FePc and its effect on the oxygen reduction reaction (ORR). It was observed that FePc was preferentially incorporated inside the porous structure, especially in samples with more developed microporosity. However, functionalization with melamine modified the textural properties and the surface chemistry, favoring the incorporation of FePc on the surface. Regarding the electrochemical performance, the presence of FePc greatly enhanced the electroactivity of the microporous catalysts. An onset potential of 0.88 V and a four-electron pathway were obtained for glucose-derived carbons, whereas the limiting current densities and kinetic current densities rose by 126% and 222%, respectively, in comparison to the base sample. Notwithstanding, the highest electrochemical activity was observed for the sample prepared with CNTs, due to the synergy between the active metal centers and their highly graphitic carbon structure. The electrochemical parameters of CNT<inf>FePc</inf> surpass the commercial Pt/C. The half-wave potential is 40 mV higher, the limiting current density increases by 17%, and a negligible production of by-products (< 1%) was observed. |
|---|