Debris extrusion and foraminal deformation produced by reciprocating instruments made of thermally treated NiTi wires
Objective: To evaluate the amount of apically extruded debris, percentage of foraminal enlargement and apical foramen (AF) deformation that occurred during root canal preparation with different reciprocation systems: Reciproc, WaveOne (M-Wire), and ProDesign R (Shape Memory Technology Wire) at two d...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2018 |
| País: | Brasil |
| Institución: | Universidade Federal do Ceará (UFC) |
| Repositorio: | Repositório Institucional da Universidade Federal do Ceará (UFC) |
| Idioma: | inglés |
| OAI Identifier: | oai:repositorio.ufc.br:riufc/40088 |
| Acceso en línea: | http://www.repositorio.ufc.br/handle/riufc/40088 |
| Access Level: | acceso abierto |
| Palabra clave: | Endodontia Endodontics Titânio Cavidade Pulpar Dental Pulp Cavity |
| Sumario: | Objective: To evaluate the amount of apically extruded debris, percentage of foraminal enlargement and apical foramen (AF) deformation that occurred during root canal preparation with different reciprocation systems: Reciproc, WaveOne (M-Wire), and ProDesign R (Shape Memory Technology Wire) at two different working lengths (WLs): 0.0 and 1.0 mm beyond the AF. Material and methods: The AF of 120 root canals in 60 mesial roots of mandibular molars were photographed with stereomicroscope and randomly assigned into four groups: manual, Reciproc (REC), WaveOne (WO), and ProDesign R (PDR); subsequently, they were further subdivided according to the WL (n=15). Teeth were instrumented, coupled to a dual collecting chamber, and then another photograph of each AF was captured. Extrusion was analysed by determining the weight of extruded debris. Each AF diameter was measured in pre- and post-instrumentation images to determine deformation, which was analysed, and afterwards the final format of AFs was classified (circular/oval/deformed). Results: We found no significant differences when analysing each system at different WLs. When considering each WL, REC and WO showed highest extrusion values (P<.05); for AF enlargement, differences were observed only for WO, when it was used beyond the AF; differences were observed among M-Wire groups beyond the AF (P<.05). AF deformation was observed in all groups; PDR showed the lowest AF deformation values at both WLs; M-Wire groups showed 50% strain beyond the AF. Conclusion: Authors concluded that beyond the apical limit, the alloy and taper are important aspects when considering extrusion and deformation. |
|---|