Preparation and characterization of a homemade Josephson junction prepared from a thin film sintered in a domestic microwave oven
A homemade Josephson junction was successfully obtained using a superconductor thin film of the BSCCO system. The film was deposited on a lanthanum aluminate, produced from a commercial powder with a nominal composition Bi1.8Pb0.4Sr2CaCu2Ox, was thermally treated by a domestic microwave oven. The XR...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2016 |
| País: | Brasil |
| Institución: | Universidade Estadual Paulista (UNESP) |
| Repositorio: | Repositório Institucional da UNESP |
| Idioma: | inglés |
| OAI Identifier: | oai:repositorio.unesp.br:11449/172799 |
| Acceso en línea: | http://dx.doi.org/10.1590/1980-5373-MR-2015-0475 http://hdl.handle.net/11449/172799 |
| Access Level: | acceso abierto |
| Palabra clave: | BPSCCO superconductor thin films Josephson junction Microwave oven |
| Sumario: | A homemade Josephson junction was successfully obtained using a superconductor thin film of the BSCCO system. The film was deposited on a lanthanum aluminate, produced from a commercial powder with a nominal composition Bi1.8Pb0.4Sr2CaCu2Ox, was thermally treated by a domestic microwave oven. The XRD analysis of the film indicated the coexistence of Bi-2212 and Bi-2223 phases and SEM images revealed that a typical superconductor plate-like morphology was formed. From the electrical characterization, performed using DC four probes technique, it was observed an onset superconducting transition temperature measured around 81K. At the current-voltage characteristics curve, a step of electric current at zero-voltage could be observed, an indicative that the tunneling Josephson °Ccurred. |
|---|