Effect of Equal Channel Angular Pressing (ECAP) on microstructure and properties of Al-FeAlCr intermetallic phase composites
An aluminium matrix composite was prepared by mixing commercial aluminium powders and 15 vol % of FeAlCr powders and consolidation by hot extrusion. The extruded composite was subjected to severe plastic deformation by equal channel angular pressing (ECAP) at room temperature and at 150°C. The extru...
| Autores: | , , , |
|---|---|
| Formato: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2014 |
| País: | Brasil |
| Recursos: | Universidade Federal de São Paulo (UNIFESP) |
| Repositorio: | Repositório Institucional da UNIFESP |
| Idioma: | inglés |
| OAI Identifier: | oai:repositorio.unifesp.br:11600/8395 |
| Acesso em linha: | http://dx.doi.org/10.1590/S1516-14392014005000029 http://repositorio.unifesp.br/handle/11600/8395 |
| Access Level: | acceso abierto |
| Palavra-chave: | ECAP composite aluminium intermetallic |
| Resumo: | An aluminium matrix composite was prepared by mixing commercial aluminium powders and 15 vol % of FeAlCr powders and consolidation by hot extrusion. The extruded composite was subjected to severe plastic deformation by equal channel angular pressing (ECAP) at room temperature and at 150°C. The extruded composite presents a uniform distribution of particles although some defects are observed such as residual pores and particle agglomerates. The particle distribution does not show a significant change due to ECAP. The extruded composite exhibits a relatively fine grain size of the order of 1-2 μm that was refined to 550 nm after three ECAP passes at room temperature by route A and to 636 nm after four passes at 150°C by route Bc. The yield stress of the composites was increased by 140 to 180% after ECAP as compared with the extruded condition. |
|---|