Photoelectrochemical characterization of ITO/TiO2 electrodes obtained by cathodic electrodeposition from aqueous solution
In the present work, the photoelectrochemical characterization of ITO/TiO2 electrodes electrosynthesized at two distinct TiO2 film charges (0.35 and 1.00 C) was performed. Scanning electron microscopy presented a globular-like nanostructure and a typical morphology that are dependent on the growing...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2015 |
| País: | Brasil |
| Institución: | Universidade Estadual Paulista (UNESP) |
| Repositorio: | Repositório Institucional da UNESP |
| Idioma: | inglés |
| OAI Identifier: | oai:repositorio.unesp.br:11449/164690 |
| Acceso en línea: | http://dx.doi.org/10.1007/s10008-015-2848-1 http://hdl.handle.net/11449/164690 |
| Access Level: | acceso abierto |
| Palabra clave: | Photoanodes ITO/TiO2 electrodes Cathodic electrodeposition Electrochemical impedance spectroscopy |
| Sumario: | In the present work, the photoelectrochemical characterization of ITO/TiO2 electrodes electrosynthesized at two distinct TiO2 film charges (0.35 and 1.00 C) was performed. Scanning electron microscopy presented a globular-like nanostructure and a typical morphology that are dependent on the growing charge, where the photoelectrode synthesized at 0.35 C presented a more homogeneous morphology. Such dependence was also observed at the photoelectrochemical response, once the photoactivity for the photoelectrode synthesized at 0.35 C was better than the photoelectrode synthesized at 1.00 C, which was explained by the surface recombination process and the electron lifetime. In order to explore the charge-transfer process and the displacement of the quasi-Fermi level upon illumination, electrochemical impedance spectroscopy (EIS) was performed at distinct applied potentials. EIS results corroborate the previous results, presenting a higher charge-transfer resistance and a lower chemical capacitance for the 1.00 C electrode film, the last one in accordance with the open-circuit voltage decay. |
|---|