Optical characterization of europium-doped indium hydroxide nanocubes obtained by Microwave-Assisted Hydrothermal method
Crystalline europium-doped indium hydroxide (In(OH)3:Eu) nanostructures were prepared by rapid and efficient Microwave-Assisted Hydrothermal (MAH) method. Nanostructures were obtained at low temperature. FE-SEM images confirm that these samples are composed of 3D nanostructures. XRD, optical diffuse...
| Autores: | , , , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2014 |
| País: | Brasil |
| Institución: | Universidade Federal do Rio Grande do Norte (UFRN) |
| Repositorio: | Repositório Institucional da UFRN |
| Idioma: | inglés |
| OAI Identifier: | oai:repositorio.ufrn.br:123456789/32084 |
| Acceso en línea: | https://repositorio.ufrn.br/handle/123456789/32084 |
| Access Level: | acceso abierto |
| Palabra clave: | Indium hydroxide Europium Microwave-Assisted Hydrothermal Nanostructures |
| Sumario: | Crystalline europium-doped indium hydroxide (In(OH)3:Eu) nanostructures were prepared by rapid and efficient Microwave-Assisted Hydrothermal (MAH) method. Nanostructures were obtained at low temperature. FE-SEM images confirm that these samples are composed of 3D nanostructures. XRD, optical diffuse reflectance and photoluminescence (PL) measurements were used to characterize the products. Emission spectra of europium-doped indium hydroxide (IH:xEu) samples under excitation (350.7 nm) presented broad band emission regarding the indium hydroxide (IH) matrix and 5D0 → 7F0, 5D0 → 7F1, 5D0 → 7F2, 5D0 → 7F3 and 5D0 → 7F4 europium transitions at 582, 596, 618, 653 and 701 nm, respectively. Relative intensities of Eu3+ emissions increased as the concentration of this ion increased from 0, 1, 2, 4 and 8 mol %, of Eu3+, but the luminescence is drastically quenched for the IH matrix |
|---|