Long-term bond strength of adhesive systems applied to etched and deproteinized dentin
The aim of this study was to evaluate the early and 12-month bond strength of two adhesive systems (Single Bond-SB and One Step-OS) applied to demineralized dentin (WH) and demineralized/NaOCl-treated dentin (H). Twenty flat dentin surfaces were exposed, etched, rinsed and slightly dried. For the H...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2007 |
| País: | Brasil |
| Institución: | Universidade de São Paulo (USP) |
| Repositorio: | Journal of applied oral science (Online) |
| Idioma: | inglés |
| OAI Identifier: | oai:revistas.usp.br:article/3515 |
| Acceso en línea: | https://www.revistas.usp.br/jaos/article/view/3515 |
| Access Level: | acceso abierto |
| Palabra clave: | Dentin-bonding agents Dentin Tensile strength |
| Sumario: | The aim of this study was to evaluate the early and 12-month bond strength of two adhesive systems (Single Bond-SB and One Step-OS) applied to demineralized dentin (WH) and demineralized/NaOCl-treated dentin (H). Twenty flat dentin surfaces were exposed, etched, rinsed and slightly dried. For the H groups, a solution of 10% NaOCl was applied for 60 s, rinsed (15 s) and slightly dried. The adhesives were applied according to the manufacturer's instructions and composite resin crowns were incrementally constructed. After 24 h (water-37ºC), the specimens was sectioned in order to obtain resin-dentin sticks (0.8 mm²). The specimens were tested in microtensile (0.5 mm/min) immediately (IM) or after 12 months of water storage (12M). The data (MPa) were subjected to ANOVA and Tukey's test (a=0.05). Only the main factors adhesive and time were significant (p=0.004 and p=0.003, respectively). SB (42.3±9.1) showed higher bond strengths than OS (33.6±11.6). The mean bond strength for IM-group (42.5±8.7) was statistically superior to 12M (33.3±11.8). The use of 10% NaOCl, after acid etching, did not improve the immediate and the long-term resin-dentin bond strength. |
|---|