Reação de precipitação de Ag na liga Cu-8%Al-6%Ag
Ag precipitation reaction in the Cu-8wt.%Al-6wt.%Ag alloys was studied using microhardness measurements with temperature and ageing time, X-ray diffraction patterns (DRX), differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). The results obtained showed that the mechanism o...
| Authors: | , , |
|---|---|
| Format: | article |
| Status: | Published version |
| Publication Date: | 2008 |
| Country: | Brasil |
| Institution: | Universidade Estadual Paulista (UNESP) |
| Repository: | Repositório Institucional da UNESP |
| Language: | Portuguese |
| OAI Identifier: | oai:repositorio.unesp.br:11449/222665 |
| Online Access: | http://dx.doi.org/10.26850/1678-4618EQJ.V33.1.2008.P63-70 http://hdl.handle.net/11449/222665 |
| Access Level: | Open access |
| Keyword: | Ag additions Cu based alloys Microhardness |
| Summary: | Ag precipitation reaction in the Cu-8wt.%Al-6wt.%Ag alloys was studied using microhardness measurements with temperature and ageing time, X-ray diffraction patterns (DRX), differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). The results obtained showed that the mechanism of Ag precipitation reaction is an Ag diffusion controlled process and reaction rate reaches a maximum at about 500ºC. |
|---|