Study of the pigment type effect on the corrosion behaviour of epoxy painted steel/sea water systems
The effect of different kind of pigments on the corrosion resistance properties of an epoxy paint has been investigated using electrochemical impedance spectroscopy and open circuit potential measurements. Painted naval steel samples were studied during the exposure to artificial sea water. The epox...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 1999 |
| País: | Argentina |
| Institución: | Consejo Nacional de Investigaciones Científicas y Técnicas |
| Repositorio: | CONICET Digital (CONICET) |
| Idioma: | inglés |
| OAI Identifier: | oai:ri.conicet.gov.ar:11336/152052 |
| Acceso en línea: | http://hdl.handle.net/11336/152052 |
| Access Level: | acceso abierto |
| Palabra clave: | CORROSION PREVENTION EPOXY COATINGS PIGMENTS SEA WATER STEEL https://purl.org/becyt/ford/2.5 https://purl.org/becyt/ford/2 |
| Sumario: | The effect of different kind of pigments on the corrosion resistance properties of an epoxy paint has been investigated using electrochemical impedance spectroscopy and open circuit potential measurements. Painted naval steel samples were studied during the exposure to artificial sea water. The epoxy paint coatings were prepared employing red lead, zinc, red iron oxide or titanium dioxide as pigment with 0.8 of PVC/CPVC ratio. From the EIS and corrosion potential data analysis was found that the anticorrosive protection given by an anticorrosive (pigmented with red lead) and a top coat (pigmented with red iron oxide) epoxy painting scheme was both more lasting and more effective. This was attributed to the fact that both the effective adhesion provided by the chemical bonding between the steel surface and the epoxy paint groups and the constant high barrier effect afforded by this type of top coat were a perfect complement for the high corrosion inhibitive capacity of the red lead pigment. |
|---|