Corrosion Performance of Conversion Treatments for Electrogalvanised Steel Sheet
Chromate conversion treatments have been widely used due to their excellent corrosion resistance properties; however, their use is increasingly restricted because of the highly toxic chromic acid solutions required, with consequent effluent disposal and ecological problems. The removal of these toxi...
| Autores: | , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2019 |
| País: | Argentina |
| Institución: | Universidad Nacional de La Plata |
| Repositorio: | SEDICI (UNLP) |
| Idioma: | inglés |
| OAI Identifier: | oai:sedici.unlp.edu.ar:10915/119304 |
| Acceso en línea: | http://sedici.unlp.edu.ar/handle/10915/119304 |
| Access Level: | acceso abierto |
| Palabra clave: | Ingeniería en Materiales Pre-treatments Conversion coatings Corrosión EIS Electrogalvanised steel |
| Sumario: | Chromate conversion treatments have been widely used due to their excellent corrosion resistance properties; however, their use is increasingly restricted because of the highly toxic chromic acid solutions required, with consequent effluent disposal and ecological problems. The removal of these toxic chemicals is considered a priority within most of the developed countries. In this work, the corrosion resistance of different alternative pretreatments applied on electrogalvanised steel sheet: 1) Cr(III) and Zr complexes layer, 2) Ce(III) layer, 3) Ce(III)/Ce(IV) double layer, 4) Cr(VI) chromating was investigated, and its results compared with those from the tests performed using bare electrogalvanized steel sheets as a substrate. These samples were exposed to aerated 0.05 mol/L NaCl or 0.1 mol/L Na2SO4 solutions. The electrochemical behavior of samples was studied by electrochemical techniques. For three days of immersion in the solution test, the experimental results have shown that, compared with the Cr(VI) protective properties, the Cr(III) + Zr complex layer presented similar performance. Even though the initial corrosion resistance was offered by the Ce(III) and Ce(VI)/Ce(III) conversion coatings was relatively good, it quickly decreased as a function of the exposure time. |
|---|