A Combined Scanning Tunneling Microscopy and Electrochemical Study of Nickel Electrodeposition on β-Brass
The electrodeposition of Ni on β-brass from Watt's bath was studied by using electrochemical techniques, scanning tunneling microscopy (STM) imaging, and X-ray diffraction. As the electrodeposition current density j was increased from 0.01 to 0.25 A cm<sup>-2</sup>, both the Ni crys...
| Autores: | , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 1996 |
| País: | Argentina |
| Institución: | Universidad Nacional de La Plata |
| Repositorio: | SEDICI (UNLP) |
| Idioma: | inglés |
| OAI Identifier: | oai:sedici.unlp.edu.ar:10915/119342 |
| Acceso en línea: | http://sedici.unlp.edu.ar/handle/10915/119342 |
| Access Level: | acceso abierto |
| Palabra clave: | Ciencias Exactas Química Ni β-brass Scanning tunneling microscopy |
| Sumario: | The electrodeposition of Ni on β-brass from Watt's bath was studied by using electrochemical techniques, scanning tunneling microscopy (STM) imaging, and X-ray diffraction. As the electrodeposition current density j was increased from 0.01 to 0.25 A cm<sup>-2</sup>, both the Ni crystal size (d) and the root mean square roughness of the deposit (ξ) decreased. For j > 0.25 A cm<sup>-2</sup> the deposit became rougher due to the growth of large Ni crystals over a background of small Ni crystals. This change in the growth mode appears as a transition in the value of ξ which is promoted by strongly adsorbed intermediates involved in the discharge of Ni<sup>2+</sup> ions. The analysis of the dynamic and static roughening exponents resulting from the application of the dynamic scaling theory to the STM images of Ni deposits indicates that the growth of Ni at high current density, i.e. far from the thermodynamic equilibrium, can be described as an aggregation process with a significant contribution of Ni atom surface diffusion. |
|---|