Eco-friendly PVA-chitosan adsorbent films for the removal of azo dye Acid Orange 7: physical cross-linking, adsorption process, and reuse of the material
The treatment of wastewater requires the use of eco-friendly and cost-efficient adsorbents. A hybrid adsorbent film based on biodegradable polymers (poly(vinyl alcohol) (PVA) and chitosan (Ch) was developed to remove Acid Orange 7 (AO7), an azo dye from the textile industry present in industrial was...
| Autores: | , , , |
|---|---|
| Formato: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2023 |
| País: | Argentina |
| Recursos: | Universidad Nacional de La Plata |
| Repositorio: | SEDICI (UNLP) |
| Idioma: | inglés |
| OAI Identifier: | oai:sedici.unlp.edu.ar:10915/160428 |
| Acesso em linha: | http://sedici.unlp.edu.ar/handle/10915/160428 |
| Access Level: | acceso abierto |
| Palavra-chave: | Química Hybrid film Biosorbent Azo dye Chitosan PVA Physical cross-linking |
| Resumo: | The treatment of wastewater requires the use of eco-friendly and cost-efficient adsorbents. A hybrid adsorbent film based on biodegradable polymers (poly(vinyl alcohol) (PVA) and chitosan (Ch) was developed to remove Acid Orange 7 (AO7), an azo dye from the textile industry present in industrial wastewaters. The polymeric absorbent material was submitted to a curing process with different timetemperature combinations which improved its physical stability in aqueous media. This result was supported by modulated differential scanning calorimetry (MDSC) and thermogravimetric analysis (TGA). ATR-FTIR also confirmed the electrostatic interactions by hydrogen bonds between PVA and Ch, as well as among the polymers and the dye. The best curing condition to reach a high removal without weight loss was the combination of 160 C-1h. Dye adsorption depended mainly on pH, adsorbent dose, contact time, temperature, and coexisting anions. The maximum removal efficiency (>91%) was achieved at pH ¼ 2.5. The adsorption kinetics followed the Lagergren pseudo first-order rate equation and the adsorption isotherm was best described by the Redlich-Peterson model. As far as the authors know, the maximum adsorption capacity (Qm) of the adsorbent film obtained in the present work is the highest value reported in literature (Qm ¼ 678 mg/g at 298 K and pH ¼ 2.5). Physisorption would be the dominant mechanism at pH 4.0 while at pH 2.5 the process was conducted by chemisorption. Regeneration studies showed that composites could be used for five consecutive cycles without losing their adsorption capacity. Thus, the use of the developed eco-compatible biodegradable materials would allow easy regeneration without losing removal selectivity, a key feature in the development of environmentally friendly sorbent materials. |
|---|