Designing an Ab2-type alloy (TIZr-CrMNMO) for the hybrid hydrogen storage concept
The hybrid hydrogen storage method consists of the combination of both solid-state metal hydrides and gas hydrogen storage. This method is regarded as a promising trade-off solution between the already developed high-pressure storage reservoir, utilized in the automobile industry, and solid-state st...
| Autores: | , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2020 |
| País: | Argentina |
| Institución: | Consejo Nacional de Investigaciones Científicas y Técnicas |
| Repositorio: | CONICET Digital (CONICET) |
| Idioma: | inglés |
| OAI Identifier: | oai:ri.conicet.gov.ar:11336/126699 |
| Acceso en línea: | http://hdl.handle.net/11336/126699 |
| Access Level: | acceso abierto |
| Palabra clave: | AB2 ALLOY COMPRESSED HYDROGEN HYBRID HYDROGEN STORAGE KINETICS METAL HYDRIDE THERMODYNAMICS https://purl.org/becyt/ford/2.5 https://purl.org/becyt/ford/2 |
| Sumario: | The hybrid hydrogen storage method consists of the combination of both solid-state metal hydrides and gas hydrogen storage. This method is regarded as a promising trade-off solution between the already developed high-pressure storage reservoir, utilized in the automobile industry, and solid-state storage through the formation of metal hydrides. Therefore, it is possible to lower the hydrogen pressure and to increase the hydrogen volumetric density. In this work, we design a non-stoichiometric AB2 C14-Laves alloy composed of (Ti0.9Zr0.1)1.25Cr0.85Mn1.1Mo0.05. This alloy is synthesized by arc-melting, and the thermodynamic and kinetic behaviors are evaluated in a high-pressure Sieverts apparatus. Proper thermodynamic parameters are obtained in the range of temperature and pressure from 3 to 85 ◦C and from 15 to 500 bar: ∆Habs. = 22 ± 1 kJ/mol H2, ∆Sabs. = 107 ± 2 J/K mol H2, and ∆Hdes. = 24 ± 1 kJ/mol H2, ∆Sdes. = 110 ± 3 J/K mol H2. The addition of 10 wt.% of expanded natural graphite (ENG) allows the improvement of the heat transfer properties, showing a reversible capacity of about 1.5 wt.%, cycling stability and hydrogenation/dehydrogenation times between 25 to 70 s. The feasibility for the utilization of the designed material in a high-pressure tank is also evaluated, considering practical design parameters. |
|---|