Nitrogen diffusion in nitrogen-doped yttria stabilised zirconia
Nitrogen self-diffusion was measured in single crystalline nitrogen-doped yttria-stabilised zirconia (YZrON) containing 10 mol% yttrium oxide. Samples containing two different nitrogen contents (5 and 6 mol% N on the anion sublattice) were investigated as a function of temperature (650-1000 K) using...
| Autores: | , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2004 |
| País: | Argentina |
| Institución: | Consejo Nacional de Investigaciones Científicas y Técnicas |
| Repositorio: | CONICET Digital (CONICET) |
| Idioma: | inglés |
| OAI Identifier: | oai:ri.conicet.gov.ar:11336/74366 |
| Acceso en línea: | http://hdl.handle.net/11336/74366 |
| Access Level: | acceso abierto |
| Palabra clave: | Nitrogen diffusion SIMS https://purl.org/becyt/ford/1.3 https://purl.org/becyt/ford/1 |
| Sumario: | Nitrogen self-diffusion was measured in single crystalline nitrogen-doped yttria-stabilised zirconia (YZrON) containing 10 mol% yttrium oxide. Samples containing two different nitrogen contents (5 and 6 mol% N on the anion sublattice) were investigated as a function of temperature (650-1000 K) using implanted N as a stable tracer. For a given temperature, the nitrogen diffusivity was nearly independent of the nitrogen content in the nitrogen-doped yttria-stabilised zirconia, which can be only partially understood using defect chemistry. The activation enthalpy of nitrogen diffusion was between 2 and 2.5 eV with a preexponential factor of the order of 100 cm2 s-1, which corresponds to a migration entropy of 5 kB. The surface exchange reaction between nitrogen and the oxonitride surface was investigated at 1073 K using 200 mbar gaseous 15N2 and was found to be slow but considerable. Decreasing the oxygen content in the gas phase can enhance the nitrogen incorporation into the oxonitrides. |
|---|