Synthesis and characterization of ZSM-5 coatings onto cordierite honeycomb supports
Zeolite ZSM-5 layers (up to ca. 30% by weight) have been synthesized on cordierite substrates, following either a direct hydrothermal synthesis procedure or a secondary growth method, in this case after seeding of the support. The Si/Al ratio in the synthesis gel ranged from 14 to 100, but layers wi...
| Autores: | , , , , , |
|---|---|
| Tipo de documento: | artigo |
| Estado: | Versão publicada |
| Data de publicação: | 2003 |
| País: | Argentina |
| Recursos: | Consejo Nacional de Investigaciones Científicas y Técnicas |
| Repositório: | CONICET Digital (CONICET) |
| Idioma: | inglês |
| OAI Identifier: | oai:ri.conicet.gov.ar:11336/40095 |
| Acesso em linha: | http://hdl.handle.net/11336/40095 |
| Access Level: | Acceso aberto |
| Palavra-chave: | Zeolite Coatings Monolith Substrates Si/Al Ratio https://purl.org/becyt/ford/2.4 https://purl.org/becyt/ford/2 |
| Resumo: | Zeolite ZSM-5 layers (up to ca. 30% by weight) have been synthesized on cordierite substrates, following either a direct hydrothermal synthesis procedure or a secondary growth method, in this case after seeding of the support. The Si/Al ratio in the synthesis gel ranged from 14 to 100, but layers with a high Al content (i.e. a low Si/Al ratio) could not be prepared directly on the cordierite support. However, MFI layers with a low Si/Al ratio were readily grown after depositing an intermediate Si-rich layer. The results also show that the Si/Al ratio of the synthesis gel has a direct effect on the morphology, crystallinity and orientation of the MFI layer formed. |
|---|