Fluidised-bed incineration bottom ash as the sole precursor of alkali-activated binders: A comparison with bottom ash from grate incinerators
The novel formulation of alkali-activated binders (AABs) using incineration bottom ash (IBA) from fluidised bed (FB) combustion technology as a sole precursor was assessed. In addition, IBA-FB was compared with IBA from moving grate (IBA-MG) combustion technology. The AABs formulated with IBA-FB (AA...
| Autores: | , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2022 |
| País: | España |
| Institución: | Universidad de Barcelona |
| Repositorio: | Dipòsit Digital de la UB |
| OAI Identifier: | oai:diposit.ub.edu:2445/196311 |
| Acceso en línea: | https://hdl.handle.net/2445/196311 |
| Access Level: | acceso abierto |
| Palabra clave: | Incineració Materials de construcció Residus Incineration Building materials Waste products |
| Sumario: | The novel formulation of alkali-activated binders (AABs) using incineration bottom ash (IBA) from fluidised bed (FB) combustion technology as a sole precursor was assessed. In addition, IBA-FB was compared with IBA from moving grate (IBA-MG) combustion technology. The AABs formulated with IBA-FB (AAB-FB) and IBA-MG (AAB-MG) were also evaluated from a physicochemical, mechanical, and environmental perspective. The results revealed that specific surface area in IBA-FB hinders the retention of kneading water of fresh pastes, affecting the workability, consistency, porosity, and mechanical strength of AAB-FB. Moreover, the low calcium content of IBA-FB requires that the formulated AABs must be cured at higher curing temperatures to ensure the formation of (N,C) ASH gels, while the high calcium content of IBA-MG promotes the formation of CSH gels at room temperature. The compressive strength results demonstrated that AAB-MG (≈ 11 MPa) and AAB-FB (≈ 8 MPa) could be used for non-structural purposes. |
|---|